PRODUCT TYPE
strong-acid cation exchange resin.
|
|
APPLICATION:
This type of resin is suitable for alkaline extraction, condensate purification, treatment of water with high chlorine concentration. |
It is characterized by oxidation-resistance, bursting-resistance, osmotic blow – resistance. Can be used in mixed layers. |
PHYSICAL AND CHEMICAL PARAMETERS
| Appearance |
transparent whitish beads* |
| Structure |
gel |
| Polymer matrix |
polystyrene - divinylbenzene |
| Functional group |
sulphonic acid |
| Ion form |
Na+ |
| Moisture, % |
40,0 |
| Total exchange capacity, meq/ml3 |
2,2 |
| Bulk density, g/ml |
0,865 |
| Particle size, mm |
0,50-1,20 |
| Effective particle size, mm |
0,57 |
| Uniformity coefficient |
1,5 |
| Volumetric part of fraction, % |
96 |
| Storage period, year |
2 |
| Storage temperature, îÑ |
-20… +120 |
*- black-colored beads can be produced according to the Customer’s requirements.
RECOMMENDED RATES AT OPERATION PROCESS
| Max. process temperature, îÑ |
120 |
| Process range of acidity, ðÍ |
1-14 |
| Layer height, mm |
800; suitable for mixed layers |
| Linear speed at operation, m/h |
10-15 |
RECOMMENDED RATES AT REGENERATION PROCESS
| Regenerating media (RM) |
NaCl |
HCl |
H2SO4 |
| Quantity of RM, g RM/l of resin |
90 |
60-100 |
60-150 |
| RM Concentration, % |
8-10 |
4-10 |
0,5-5 |
| Consumption of regeneration, RM volume/ resin volume |
1,5-2:1 |
2-3:1 |
10-20:1 |
| Linear speed at regeneration process, m/h |
4-6 |
4-6 |
10-15 |
| Contact period at regeneration process, min. |
30 |
| Linear speed at washing process, m/h |
10-20 |
| Contact period of washing process, min. |
20-40 |
| Volume change, Na+ → H+,% |
8-10 |
INTERNATIONAL EQUIVALENTS
Purolite C-100*10, Amberlite IR-122, Russian standard ÊÓ-2-8 ÔÑÄ |